MY-132-V15K: Optical Coating /Adhesive
MY-132-V-15K is a low refractive index UV curable coating/recoating/adhesive. Its main feature is the low refractive index of 1.322 at 950 nm. MY-132-V15K is a tacky polymer, with much better adhesion compared to both MY-132 and MY-132-A.
A typical application is the lamination of 2 flat surfaces or films.
Properties
| Liquid state | |
| RI liquid at 589 nm | 1.326 |
| Density, g/cm3 | 1.73 |
| Viscosity, cps @ 25°C | 14500 |
| Cured state | |
| RI cured at 589 nm | 1.327 |
| RI cured at 950 nm | 1.322 |
| Adhesion to glass, 90° Peel, g/cm | 40 |
| Elastic modulus, MPa | |
| Tensile Strength, MPa | |
| Elongation at Break, % | |
| Hardness, Shore A | 7 |
| Volumetric Shrinkage, % | 0.8 |
The product is supplied pre-filtered to below 1 micron particles.
Storage
- Avoid unnecessary exposure to ambient light and moisture.
- Long term storage should be at ambient conditions of 10-30ºC.
- The coating is supplied in glass bottles. Keep container closed to avoid moisture penetration.
- The shelf life is 12 months.
Application
Curing can be achieved by any source of UV at 300-400nm. Typically, a dose of 1000-2000 mJ/cm2 is necessary.
Keep the bottle closed in all times when not in use. The material is sensitive to light.
Safety: Refer to the SDS
Note: The above information is believed to be reliable, but it is not to be taken as a representation, warrantee or guarantee. Customers should perform their own QC, QA and evaluation tests.
Updated: August 7, 2018