OF-140-N3
OF-140-N3 is a low refractive index optical fiber coating, developed for the cladding of optical fibers. The material is designed to be used in Optical fiber Drawing Towers.
OF-140-N3 is a new version of OF-140-N. It has better adhesion and higher modulus. In addition, OF-140-N3 does not have the strong acidic odor of OF-140-N. It should provide a more comfortable working environment.
Properties
| Liquid state | |
| RI liquid at 589 nm | 1.396 |
| Density, g/cm3 | 1.43 |
| Viscosity, cps @ 25°C | 3700 |
| Cured state | |
| RI cured at 589 nm | 1.409 |
| RI cured at 950 nm | 1.402 |
| Adhesion to glass, 90° Peel, g/cm | 150 |
| Elastic modulus, MPa | 330 |
| Tensile Strength, MPa | 11 |
| Elongation at Break, % | 40 |
The product is supplied pre-filtered to below 1-micron particles.
Storage
- Avoid unnecessary exposure to ambient light and moisture.
- Long-term storage should be at ambient conditions of 10-30ºC.
- The coating is supplied in glass bottles. Keep the container closed to avoid moisture penetration.
- The shelf life is 12 months.
Application
OF-140-N3 is intended to be used in optical fiber drawing towers. UV curing is done under nitrogen. Typically, a dose of 1000-2000 mJ/cm2 is necessary. Any UV source in the range of 300-400 nm can be used. When properly cured under nitrogen, the surface should be non-tacky.
Keep the bottle closed at all times when not in use. The material is sensitive to light.
Safety: Refer to the SDS
Note: The above information is believed to be reliable, but it is not to be taken as a representation, warranty, or guarantee. Customers should perform their own QC, QA, and evaluation tests.
Updated: October 16, 2023