OF-136: Optical Fiber Primary Coating
OF-136 is a low refractive index primary coating material, developed for the cladding of optical fibers. The material is designed to be compatible with Optical fiber Drawing Towers.
OF-136 includes a proprietary adhesion promoter that improves adhesion to the silica core of the fiber, especially under wet conditions (e.g. hot water immersion test). It was designed to enable significantly longer shelf life, compared to previously available adhesion promoters.
Properties
| Liquid state | |
| RI liquid at 589 nm | 1.359 |
| Density, g/cm3 | 1.58 |
| Viscosity, cps @ 25°C | 2200 |
| Cured state | |
| RI cured at 589 nm | 1.369 |
| RI cured at 950 nm | 1.363 |
| Adhesion to glass, 90° Peel, g/cm | 64 |
| Elastic modulus, MPa | 85 |
| Tensile Strength, MPa | 8 |
| Elongation at Break, % | 50 |
The product is supplied pre-filtered to below 1 micron particles.
Storage
- Avoid unnecessary exposure to ambient light and
- Long-term storage should be at ambient conditions of 10-30ºC.
- The coating is supplied in glass bottles. Keep the container closed to avoid moisture
- The shelf life is 6
Application
OF-136 is intended to be used in optical fiber drawing towers. The UV curing is done under nitrogen. Typically, a dose of 1000-2000 mJ/cm2 is necessary. Any UV source in the 300-400 nm range can be used. When properly cured under nitrogen, the surface should be non-tacky.
Keep the bottle closed at all times when not in use. The material is sensitive to both light and moisture.
Safety: Refer to the SDS
Note: The above information is believed to be reliable, but it is not to be taken as a representation, warranty, or guarantee. Customers should perform their own QC, QA, and evaluation tests.
Updated: December 28, 2016